capi32
| Inviato il: 02/09/2018 18:40:10
|
il mio diario
12/08/18 > 01h57 > Cycle_86 >C-CV 90mA>2,44V>cut-off 60mA ,p.360mm, D-CC 90mA>1,90v > 733mAh/dcm2 (Rend.0.639)
14/08/18 > 04h00 > Cycle_87 >C-CV 90mA>2,44V>cut-off 60mA ,p.360mm, D-CC 90mA>1,90v > 678mAh/dcm2 (Rend.0.615)
15/08/18 > 04h01 > Cycle_88 >C-CV 90mA>2,44V>cut-off 60mA ,p.360mm, D-CC 90mA>1,90v > 671mAh/dcm2
16/08/18 > 02h27 > Cycle_89 >C-CV 90mA>2,44V>cut-off 60mA ,p.360mm, D-CC 150mA>1,70v > 629mAh/dcm2 (Rend.0.) 1217
16/08/18 > 19h30 > Cycle_90 >C-CV 200mA>2,43V>cut-off 90mA ,C-CV 90mA>2,25V>cut-off 50mA ,p.x, D-CC 120mA>1,91v > 694mAh/dcm(Rend.0.673)
17/08/18 > 15h13 > Cycle_91 >C-CV 200mA>2,43V>c-off 190mA ,C-CV 90mA>2,25V>c-off 20mA ,p.5mm, D-CC 120mA>1,91v > 638mAh/dcm2
18/08/18 > 3h18 > Cycle_92 >C-CV 200mA>2,43V>c-off 190mA ,C-CV 90mA>2,25V>c-off 20mA ,p.5mm, D-CC 120mA>1,91v > 461mAh/dcm2
19/08/18 > 4h18 > Cycle_92 >C-CV 120mA>2,43V>c-off 110mA ,C-CV 90mA>2,25V>c-off 20mA ,p.5mm, D-CC 90mA>1,91v > 736 mAh/dcm2
19/08/18 > 5h16 > Cycle_93 >C-CV 90mA>2,1V>c-off 80mA ,C-CV 50mA>2,25V>c-off 10mA ,p.5mm, D-CC 90mA>1,90v > 752 mAh/dcm2
20/08/18 > 5h16 > Cycle_94 > coupre courant
21/08/18 > 6h15 > Cycle_95 >C-CV 90mA>2,43V>c-off 80mA ,C-CV 50mA>2,25V>c-off 10mA ,p.5mm, D-CC 90mA>1,90v > 761 mAh/dcm2
22/08/18 > 1h58 > Cycle_96 >C-CV 90mA>2,43V>c-off 80mA ,C-CV 50mA>2,25V>c-off 10mA ,p.5mm, D-CC 90mA>1,90v > 788 mAh/dcm2 (Rend.0.576)
22/08/18 > 22h14 > Cycle_97 >C-CV 90mA>2,43V>c-off 80mA ,C-CV 50mA>2,25V>c-off 10mA ,p.5mm, D-CC 90mA>1,90v > 801 mAh/dcm2(Rend.0.691)
23/08/18 > 20h52 > Cycle_98 >C-CV 90mA>2,43V>c-off 80mA ,C-CV 50mA>2,25V>c-off 10mA ,p.5mm, D-CC 90mA>1,90v > 815 mAh/dcm2(Rend.0.706)
24/08/18 > 18h52 > Cycle_99 >C-CV 90mA>2,43V>c-off 80mA ,C-CV 50mA>2,25V>c-off 10mA ,p.5mm, D-CC 90mA>1,90v > 747 mAh/dcm2(Rend.0.747)
25/08/18 > 14h32 > Cycle_100 >C-CV 90mA>2,43V>c-off 80mA ,C-CV 50mA>2,25V>c-off 10mA ,p.5mm, D-CC 90mA>1,90v > 712 mAh/dcm2
26/08/18 > 8h54 > Cycle_101 >C-CV 90mA>2,43V>c-off 80mA ,C-CV 50mA>2,25V>c-off 10mA ,p.5mm, D-CC 90mA>1,70v > 771 mAh/dcm2
27/08/18 > 4h42 > Cycle_102 >C-CV 80mA>2,43V>c-off 80mA ,C-CV 50mA>2,25V>c-off 10mA ,p.5mm, D-CC 90mA>1,90v > 735 mAh/dcm2
28/08/18 > 1h07 > Cycle_103 >C-CV 80mA>2,43V>c-off 80mA ,C-CV 50mA>2,25V>c-off 10mA ,p.5mm, D-CC 90mA>1,90v > 779 mAh/dcm2
28/08/18 > 22h27 > Cycle_104 >C-CV 80mA>2,43V>c-off 80mA ,C-CV 50mA>2,25V>c-off 10mA ,p.5mm, D-CC 90mA>1,90v > 804 mAh/dcm2
30/08/18 > 1h51 > Cycle_105 >C-CV 80mA>2,43V>c-off 80mA ,C-CV 50mA>2,25V>c-off 10mA ,p.5mm, D-CC 90mA>1,90v > 807 mAh/dcm2 (Rend.0.668)
31/08/18 > 4h50 > Cycle_106 >C-CV 80mA>2,43V>c-off 80mA ,C-CV 50mA>2,25V>c-off 10mA ,p.5mm, D-CC 90mA>1,90v > 761 mAh/dcm2 (Rend.0.729)
01/09/18 > 4h50 > Cycle_107 >C-CV 80mA>2,43V>c-off 80mA ,C-CV 50mA>2,25V>c-off 10mA ,p.5mm, D-CC 90mA>1,90v > 786 mAh/dcm2 (Rend.0.716)
01/09/18 > 23h13 > Cycle_108 >C-CV 80mA>2,43V>c-off 80mA ,C-CV 50mA>2,25V>c-off 10mA ,p.5mm, D-CC 90mA>1,90v > 785 mAh/dcm2
come ho indicato alcuni giorni fa nel post ITA, la capacità oscilla tra 730 e 800 mAh / dcm2 dopo la caduta del principio attivo.
è andata avanti per 27 cicli e sfortunatamente penso di aver raggiunto il limite di capacità sfruttabile delle batterie di tipo Plante!
ottimizzando l'acido e i parametri di carica e scarica, potrei raggiungere probabilmente 1Ah / dcm2.
ma ha una semplice scarica profonda all 80/90% causerebbe una brusca caduta di materiale e un ritorno a una capacità "normale" di 730 mAh/dcm2
Pertanto convalido il parametro di capacità massima di una batteria Planté a 750 mAh / dcm 2 di superficie positiva.
questo parametro mi consentirà di dimensionare le piastre delle mie future batterie
il test di usura continuerà fino alla distruzione delle piastre positive che (per il richiamo) sono solo 0,5 mm
Otterrei quindi la durata in base allo spessore delle piastre di piombo.
Modificato da capi32 - 02/09/2018, 20:46:55