capi32
| Inviato il: 16/12/2018 09:19:24
|
CITAZIONE (ITA815, 04/12/2018 08:06:42 ) 
Non è ancora arrivata a 900 ...
presto
il giornale:
05/12/18 > 09h06 > Cycle_B_6 >C-CV 50mA>2,25V>c-off 50mA ,C-CV 20mA>2,25V>c-off 10mA ,pause 5mm, D-CC 50mA>1,70v >354>> 708mAh/dcm2
06/12/18 > 05h20 > Cycle_B_7 >C-CV 50mA>2,25V>c-off 50mA ,C-CV 20mA>2,25V>c-off 10mA ,pause 5mm, D-CC 50mA>1,70v >362>> 724mAh/dcm2
06/12/18 > 05h21 > C-CV 50mA>2,25V>c-off 10mA,pause
08/12/18 > 17h00 > Cycle_B_8 >C-CV 50mA>2,25V>c-off 50mA ,C-CV 20mA>2,25V>c-off 10mA ,pause 5mm, D-CC 50mA>1,70v >418>> 836mAh/dcm2
09/12/18 > 17h00 > Cycle_B_9 >C-CV 50mA>2,25V>c-off 50mA ,C-CV 20mA>2,25V>c-off 10mA ,pause 5mm, D-CC 50mA>1,70v >421>> 842mAh/dcm2
09/12/18 > 17h01 > C-CV 50mA>2,25V>c-off 10mA,pause
11/12/18 > 11h15 > Cycle_B_10 >C-CV 50mA>2,25V>c-off 50mA ,C-CV 20mA>2,25V>c-off 10mA ,pause 5mm, D-CC 50mA>1,70v >416>> 832mAh/dcm2
12/12/18 > 11h15 > Cycle_B_11 >C-CV 50mA>2,25V>c-off 50mA ,C-CV 20mA>2,25V>c-off 10mA ,pause 5mm, D-CC 50mA>1,70v >412>> 824mAh/dcm2
14/12/18 > 22h00 > Cycle_B_12 >C-CV 50mA>2,25V>c-off 50mA ,C-CV 20mA>2,25V>c-off 10mA ,pause 5mm, D-CC 50mA>1,70v >438>> 876mAh/dcm2
15/12/18 > 18h42 > Cycle_B_13 >C-CV 50mA>2,25V>c-off 50mA ,C-CV 20mA>2,25V>c-off 10mA ,pause 5mm, D-CC 50mA>1,70v >435>> 870mAh/dcm2
come potete vedere nella foto, la piastra positiva non viene convertita al 100%, ci sono alcune tracce di solfato bianco.
Ho anche cambiato il filo di rame stagnato perché l'acido sale per capillarità di 3 cm.
anche la clip di coccodrillo è stata raggiunta.
attualmente la batteria è a 870mAh / dcm2 con inversione 0 sulla piastra negativa e 1 inversione sulla piastra positiva.
come promemoria, la formazione iniziale è fatta con un allenamento con acido nitrico (metodo di Mr. Epstein) che mi ha permesso di ottenere 560 mAh / dcm2 dopo 5 cicli di carica e scarica.
Lo scopo di questo test ora è sapere quanta perossido si può formare sulla piastra positiva stabilmente con una scarica dell 80 / 100%.
Immagine Allegata: IMG_4553.JPG
---------------
cugino della Francia
Inverter MPPsolar MPI 5.5Kw, 6480W pannelli, 4x100A PbCa e presto anche le batterie Planté ...
|
| | |
capi32
| Inviato il: 16/12/2018 17:36:08
|
CITAZIONE (ITA815, 04/12/2018 08:06:42 )
Non è ancora arrivata a 900 ...
Ecco
16/12/18 > 17h17 > Cycle_B_14 >C-CV 50mA>2,25V>c-off 50mA ,C-CV 20mA>2,25V>c-off 10mA ,pause 5mm, D-CC 50mA>1,70v >462>> 924mAh/dcm2
---------------
cugino della Francia
Inverter MPPsolar MPI 5.5Kw, 6480W pannelli, 4x100A PbCa e presto anche le batterie Planté ...
|
| | |
ITA815
| Inviato il: 16/12/2018 21:58:34
|
ottimo. |
| | |
capi32
| Inviato il: 23/12/2018 16:18:44
|
il log del test di usura
16/12/18 > 17h17 > Cycle_B_14 >C-CV 50mA>2,25V>c-off 50mA ,C-CV 20mA>2,25V>c-off 10mA ,pause 5mm, D-CC 50mA>1,70v >462>> 924mAh/dcm2
17/12/18 > 16h15 > Cycle_B_15 >C-CV 50mA>2,25V>c-off 50mA ,C-CV 20mA>2,25V>c-off 10mA ,pause 5mm, D-CC 50mA>1,70v >458>> 916mAh/dcm2
18/12/18 > 14h45 > Cycle_B_16 >C-CV 50mA>2,25V>c-off 50mA ,C-CV 20mA>2,25V>c-off 10mA ,pause 5mm, D-CC 50mA>1,70v >442>> 884mAh/dcm2
19/12/18 > 13h30 > Cycle_B_17 >C-CV 50mA>2,25V>c-off 50mA ,C-CV 20mA>2,25V>c-off 10mA ,pause 5mm, D-CC 50mA>1,70v >450>> 900mAh/dcm2
20/12/18 > 10h20 > Cycle_B_18 >C-CV 50mA>2,25V>c-off 50mA ,C-CV 20mA>2,25V>c-off 10mA ,pause 5mm, D-CC 50mA>1,70v >429>> 858mAh/dcm2
21/12/18 > 11h40 > Cycle_B_19 >C-CV 50mA>2,25V>c-off 50mA ,C-CV 20mA>2,25V>c-off 10mA ,pause 5mm, D-CC 50mA>1,70v >448>> 896mAh/dcm2
22/12/18 > 09h20 > Cycle_B_20 >C-CV 50mA>2,25V>c-off 50mA ,C-CV 20mA>2,25V>c-off 10mA ,pause 5mm, D-CC 50mA>1,70v >453>> 906mAh/dcm2
23/12/18 > 09h00 > Cycle_B_21 >C-CV 50mA>2,25V>c-off 50mA ,C-CV 20mA>2,25V>c-off 10mA ,pause 5mm, D-CC 50mA>1,70v >467>> 934mAh/dcm2
il mio massimo di 968 mAh / dcm2 non è ancora stato raggiunto ma tutto funziona normalmente.
niente di più da segnalare.
---------------
cugino della Francia
Inverter MPPsolar MPI 5.5Kw, 6480W pannelli, 4x100A PbCa e presto anche le batterie Planté ...
|
| | |
capi32
| Inviato il: 17/01/2019 11:16:05
|
qui si raggiunge l'obiettivo del grafico F-129
1,112 Ah/dcm2 il mio record di capacità
il giornale:
24/12/18 > 10h00 > Cycle_B_22 >C-CV 50mA>2,25V>c-off 50mA ,C-CV 50mA>2,25V>c-off 10mA ,pause 5mm, D-CC 50mA>1,70v >476>> 952mAh/dcm2
25/12/18 > 10h20 > Cycle_B_23 >C-CV 50mA>2,25V>c-off 50mA ,C-CV 50mA>2,25V>c-off 10mA ,pause 5mm, D-CC 50mA>1,70v >473>> 946mAh/dcm2
26/12/18 > 07h55 > Cycle_B_24 >C-CV 50mA>2,25V>c-off 50mA ,C-CV 50mA>2,25V>c-off 10mA ,pause 5mm, D-CC 50mA>1,70v >446>> 892mAh/dcm2
26/12/18 > 07h55 > pause
28/12/18 > 11h17 > Cycle_B_25 >C-CV 50mA>2,25V>c-off 50mA ,C-CV 50mA>2,25V>c-off 10mA ,pause 5mm, D-CC 50mA>1,70v >483>> 966mAh/dcm2
28/12/18 > 11h17 > pause
30/12/18 > 17h20 > Cycle_B_26 >C-CV 50mA>2,25V>c-off 50mA ,C-CV 50mA>2,25V>c-off 10mA ,pause 5mm, D-CC 50mA>1,70v >464>> 928mAh/dcm2
31/12/18 > 15h40 > Cycle_B_27 >C-CV 50mA>2,25V>c-off 50mA ,C-CV 50mA>2,25V>c-off 10mA ,pause 5mm, D-CC 50mA>1,70v >455>> 910mAh/dcm2
01/01/19 > 14h08 > Cycle_B_28 >C-CV 50mA>2,25V>c-off 50mA ,C-CV 50mA>2,25V>c-off 10mA ,pause 5mm, D-CC 50mA>1,70v >465>> 930mAh/dcm2
02/01/19 > 12h54 > Cycle_B_29 >C-CV 50mA>2,25V>c-off 50mA ,C-CV 50mA>2,25V>c-off 10mA ,pause 5mm, D-CC 50mA>1,70v >471>> 942mAh/dcm2
03/01/19 > 11h20 > Cycle_B_30 >C-CV 50mA>2,25V>c-off 50mA ,C-CV 50mA>2,25V>c-off 10mA ,pause 5mm, D-CC 50mA>1,70v >450>> 900mAh/dcm2
04/01/19 > 08h57 > Cycle_B_31 >C-CV 50mA>2,25V>c-off 50mA ,C-CV 50mA>2,25V>c-off 10mA ,pause 5mm, D-CC 50mA>1,70v >433>> 866mAh/dcm2
06/01/19 > 05h24 > Cycle_B_32 >C-CV 50mA>2,25V>c-off 50mA ,C-CV 50mA>2,25V>c-off 10mA ,pause 5mm, D-CC 50mA>1,70v >480>> 960mAh/dcm2
07/01/19 > 17h30 > Cycle_B_33 >C-CV 50mA>2,25V>c-off 50mA ,C-CV 50mA>2,25V>c-off 10mA ,pause 5mm, D-CC 50mA>1,70v >487>> 974mAh/dcm2
08/01/19 > 18h33 > Cycle_B_34 >C-CV 60mA>2,25V>c-off 60mA ,C-CV 60mA>2,25V>c-off 10mA ,pause 5mm, D-CC 60mA>1,70v >496>> 992mAh/dcm2
09/01/19 > 17h20 > Cycle_B_35 >C-CV 100mA>2,25V>c-off 100mA ,C-CV 60mA>2,25V>c-off 10mA ,pause 5mm, D-CC 60mA>1,70v >511>> 1022mAh/dcm2
10/01/19 > 16h20 > Cycle_B_36 >C-CV 100mA>2,25V>c-off 100mA ,C-CV 60mA>2,25V>c-off 10mA ,pause 5mm, D-CC 60mA>1,70v >494>> 988mAh/dcm2
11/01/19 > 16h20 > Cycle_B_37 >C-CV 100mA>2,25V>c-off 100mA ,C-CV 60mA>2,25V>c-off 10mA ,pause 5mm, D-CC 60mA>1,70v >485>> 970mAh/dcm2
12/01/19 > 12h14 > Cycle_B_38 >C-CV 100mA>2,25V>c-off 100mA ,C-CV 60mA>2,25V>c-off 10mA ,pause 420mm, D-CC 60mA>1,70v >516>> 1032mAh/dcm2
13/01/19 > 04h30 > Cycle_B_39 >C-CV 100mA>2,25V>c-off 100mA ,C-CV 60mA>2,25V>c-off 10mA ,pause 5mm, D-CC 60mA>1,70v >546>> 1092mAh/dcm2
16/01/19 > 09h30 > Cycle_B_40 >C-CV 100mA>2,25V>c-off 100mA ,C-CV 100mA>2,25V>c-off 10mA ,pause 810mm, D-CC 70mA>1,70v >535>> 1070mAh/dcm2
16/01/19 > 02h45 > Cycle_B_41 >C-CV 100mA>2,25V>c-off 100mA ,C-CV 100mA>2,25V>c-off 10mA ,pause xmm, D-CC 70mA>1,70v >556>> 1112mAh/dcm2
cicli di usura continui
Immagine Allegata: objectif_ok.jpg
---------------
cugino della Francia
Inverter MPPsolar MPI 5.5Kw, 6480W pannelli, 4x100A PbCa e presto anche le batterie Planté ...
|
| | |
ITA815
| Inviato il: 17/01/2019 17:57:12
|
Certo che con l' acido nitrico si fa alla svela a formare le celle. |
| | |
capi32
| Inviato il: 17/01/2019 21:06:22
|
CITAZIONE (ITA815, 17/01/2019 17:57:12 )
Certo che con l' acido nitrico si fa alla svela a formare le celle.
queste piastre erano a contatto con acido nitrico solo 2 ore e dopo più di 240 cicli di carica e scarica per quasi 7 mesi, c'è molto tempo che c'è più acido nitrico.
la cosa principale in questo test è che lo strato di perossido sul positivo è appiccicoso e questo è il caso!
Come promemoria, l'allenamento di acido nitrico che sto eseguendo è completamente diverso da quello che è stato fatto da tutti gli altri membri di questo forum.
questo trattamento converte il piombo in uno speciale nitrosonitrato di piombo che viene poi convertito in una piastra negativa, ecc.
se non sbaglio la formula è N2O4Pb
LINK
---------------
cugino della Francia
Inverter MPPsolar MPI 5.5Kw, 6480W pannelli, 4x100A PbCa e presto anche le batterie Planté ...
|
| | |
capi32
| Inviato il: 27/01/2019 12:02:21
|
ecco il mio diario
17/01/19 > 20h16 > Cycle_B_42 >C-CV 100mA>2,25V>c-off 100mA ,C-CV 100mA>2,25V>c-off 10mA ,pause 5mm, D-CC 70mA>1,70v >570>> 1140mAh/dcm2
18/01/19 > 11h40 > Cycle_B_43 >C-CV 100mA>2,25V>c-off 100mA ,C-CV 100mA>2,25V>c-off 10mA ,pause 300mm, D-CC 70mA>1,70v >536>> 1072mAh/dcm2
19/01/19 > 02h00 > Cycle_B_44 >C-CV 100mA>2,25V>c-off 100mA ,C-CV 100mA>2,25V>c-off 10mA ,pause 180mm, D-CC 70mA>1,70v >536>> 1072mAh/dcm2
20/01/19 > 02h51 > Cycle_B_45 >C-CV 100mA>2,25V>c-off 10mA ,pause 180mm ,C-CV 100mA>2,25V>c-off 10mA , D-CC 70mA>1,70v >581>> 1162mAh/dcm2
20/01/19 > 23h15 > Cycle_B_46 >C-CV 100mA>2,25V>c-off 10mA ,pause 180mm ,C-CV 100mA>2,25V>c-off 10mA , D-CC 70mA>1,70v >586>> 1172mAh/dcm2
21/01/19 > 21h27 > Cycle_B_47 >C-CV 100mA>2,25V>c-off 10mA ,pause 270mm ,C-CV 100mA>2,25V>c-off 10mA , D-CC 70mA>1,70v >591>> 1182mAh/dcm2
23/01/19 > 05h30 > Cycle_B_48 >C-CV 100mA>2,25V>c-off 10mA ,pause 270mm ,C-CV 100mA>2,25V>c-off 10mA , D-CC 70mA>1,70v >582>> 1164mAh/dcm2
24/01/19 > 03h02 > Cycle_B_49 >C-CV 100mA>2,25V>c-off 10mA ,pause 270mm ,C-CV 100mA>2,25V>c-off 10mA , D-CC 70mA>1,70v >577>> 1154mAh/dcm2
25/01/19 > 00h20 > Cycle_B_50 >C-CV 100mA>2,25V>c-off 10mA ,pause 270mm ,C-CV 100mA>2,25V>c-off 10mA , D-CC 70mA>1,70v >582>> 1164mAh/dcm2
25/01/19 > 21h30 > Cycle_B_51 >C-CV 100mA>2,25V>c-off 10mA ,pause 270mm ,C-CV 100mA>2,25V>c-off 10mA , D-CC 70mA>1,70v >597>> 1194mAh/dcm2
26/01/19 > 20h50 > Cycle_B_52 >C-CV 100mA>2,25V>c-off 10mA ,pause 270mm ,C-CV 100mA>2,25V>c-off 10mA , D-CC 70mA>1,70v >642>> 1284mAh/dcm2
come puoi vedere, le mie lastre superano il limite della curva del grafico.
nonostante le cadute di materiale e sottile, le piastre sono ancora in aumento di capacità.
Penso che ora progredirà fino alla formazione di tutto lo spessore.
Adattare i parametri di questo test per avere una carica completa in C7 (7 ore / 2,25 V) e una scarica completa in C10 (10 ore fino a 1,7 v).
queste impostazioni simulano un impianto fotovoltaico invernale (secondo le mie esigenze) e mi consentiranno di dimensionare l'area totale della piastra in base alla mia capacità di carico.
test continui
---------------
cugino della Francia
Inverter MPPsolar MPI 5.5Kw, 6480W pannelli, 4x100A PbCa e presto anche le batterie Planté ...
|
| | |
ITA815
| Inviato il: 28/01/2019 00:29:08
|
C7 è troppo per il periodo invernale ... vanno bene al limite d' estate.
Per il periodo invernale le devi portare in C5. |
| | |
ITA815
| Inviato il: 25/02/2019 11:38:35
|
Novità ? |
| | |
capi32
| Inviato il: 25/02/2019 21:57:35
|
sì, ecco le notizie:
27/01/19 > 23h12 > Cycle_B_53 >C-CV 100mA>2,25V>c-off 10mA ,pause xxxmm ,C-CV 100mA>2,25V>c-off 10mA , D-CC 70mA>1,70v >642>> 1284mAh/dcm2
28/01/19 > 23h00 > Cycle_B_54 >C-CV 100mA>2,25V>c-off 10mA ,pause 270mm ,C-CV 100mA>2,25V>c-off 10mA , D-CC 70mA>1,70v >647>> 1292mAh/dcm2
29/01/19 > 23h00 > Cycle_B_55 >C-CV 130mA>2,25V>c-off 10mA ,pause 270mm ,C-CV 100mA>2,25V>c-off 10mA , D-CC 70mA>1,70v >641>> 1282mAh/dcm2
30/01/19 > 18h43 > Cycle_B_56 >C-CV 130mA>2,25V>c-off 10mA ,pause 270mm ,C-CV 100mA>2,25V>c-off 10mA , D-CC 70mA>1,70v >633>> 1266mAh/dcm2
31/01/19 > 15h15 > Cycle_B_57 >C-CV 130mA>2,25V>c-off 10mA ,pause 270mm ,C-CV 100mA>2,25V>c-off 10mA , D-CC 70mA>1,70v >629>> 1258mAh/dcm2
01/02/19 > 13h40 > Cycle_B_58 >C-CV 130mA>2,25V>c-off 10mA ,pause 270mm ,C-CV 100mA>2,25V>c-off 10mA , D-CC 70mA>1,70v >657>> 1314mAh/dcm2
02/02/19 > 13h40 > Cycle_B_59 >C-CV 130mA>2,25V>c-off 10mA ,pause 270mm ,C-CV 100mA>2,25V>c-off 10mA , D-CC 70mA>1,70v >657>> 1314mAh/dcm2
03/02/19 > 09h20 > Cycle_B_60 >C-CV 130mA>2,25V>c-off 10mA ,pause 270mm ,C-CV 100mA>2,25V>c-off 10mA , D-CC 70mA>1,70v >629>> 1258mAh/dcm2
04/02/19 > 07h12 > Cycle_B_61 >C-CV 130mA>2,25V>c-off 10mA ,pause 270mm ,C-CV 100mA>2,25V>c-off 10mA , D-CC 70mA>1,70v >629>> 1258mAh/dcm2
05/02/19 > 04h50 > Cycle_B_62 >C-CV 130mA>2,25V>c-off 10mA ,pause 270mm ,C-CV 100mA>2,25V>c-off 10mA , D-CC 70mA>1,70v >658>> 1316mAh/dcm2
06/02/19 > 04h50 > Cycle_B_63 >C-CV 130mA>2,25V>c-off 10mA ,pause 270mm ,C-CV 100mA>2,25V>c-off 10mA , D-CC 70mA>1,70v >689>> 1378mAh/dcm2
07/02/19 > 04h10 > Cycle_B_64 >C-CV 130mA>2,25V>c-off 10mA ,pause 270mm ,C-CV 100mA>2,25V>c-off 10mA , D-CC 70mA>1,70v >684>> 1368mAh/dcm2
08/02/19 > 03h12 > Cycle_B_65 >C-CV 130mA>2,25V>c-off 10mA ,pause 270mm ,C-CV 100mA>2,25V>c-off 10mA , D-CC 70mA>1,70v >674>> 1348mAh/dcm2
09/02/19 > 03h30 > Cycle_B_66 >C-CV 130mA>2,25V>c-off 10mA ,pause 270mm ,C-CV 100mA>2,25V>c-off 10mA , D-CC 70mA>1,70v >671>> 1342mAh/dcm2
09/02/19 > 23h45 > Cycle_B_67 >C-CV 130mA>2,25V>c-off 10mA ,pause 270mm ,C-CV 100mA>2,25V>c-off 10mA , D-CC 80mA>1,70v >680>> 1360mAh/dcm2
12/02/19 > 04h10 > Cycle_B_68 >C-CV 140mA>2,25V>c-off 10mA ,pause 270mm ,C-CV 100mA>2,25V>c-off 10mA , D-CC 80mA>1,70v >663>> 1326mAh/dcm2
13/02/19 > 01h45 > Cycle_B_69 >C-CV 140mA>2,25V>c-off 10mA ,pause 270mm ,C-CV 100mA>2,25V>c-off 10mA , D-CC 80mA>1,70v >663>> 1326mAh/dcm2
13/02/19 > 23h00 > Cycle_B_70 >C-CV 140mA>2,25V>c-off 10mA ,pause 270mm ,C-CV 100mA>2,25V>c-off 10mA , D-CC 80mA>1,70v >662>> 1324mAh/dcm2
14/02/19 > 19h10 > Cycle_B_71 >C-CV 140mA>2,3V>c-off 10mA ,pause 270mm ,C-CV 100mA>2,25V>c-off 10mA , D-CC 80mA>1,70v >674>> 1348mAh/dcm2
15/02/19 > 16h10 > Cycle_B_72 >C-CV 140mA>2,3V>c-off 10mA ,pause 270mm ,C-CV 100mA>2,25V>c-off 10mA , D-CC 80mA>1,70v >658>> 1316mAh/dcm2
16/02/19 > 07h00 > Cycle_B_73 >C-CV 140mA>2,3V>c-off 10mA ,pause 270mm ,C-CV 100mA>2,25V>c-off 10mA , D-CC 80mA>1,70v >640>> 1280mAh/dcm2
17/02/19 > 08h10 > Cycle_B_74 >C-CV 140mA>2,3V>c-off 10mA ,pause 270mm ,C-CV 100mA>2,25V>c-off 10mA , D-CC 80mA>1,70v >644>> 1288mAh/dcm2
18/02/19 > 04h10 > Cycle_B_75 >C-CV 140mA>2,25V>c-off 10mA ,pause 270mm ,C-CV 100mA>2,25V>c-off 10mA , D-CC 80mA>1,70v >645>> 1290mAh/dcm2
19/02/19 > 00h35 > Cycle_B_76 >C-CV 140mA>2,25V>c-off 10mA ,pause 270mm ,C-CV 100mA>2,25V>c-off 10mA , D-CC 80mA>1,70v >647>> 1294mAh/dcm2
19/02/19 > 20h07 > Cycle_B_77 >C-CV 140mA>2,25V>c-off 10mA ,pause 270mm ,C-CV 100mA>2,25V>c-off 10mA , D-CC 80mA>1,70v >628>> 1256mAh/dcm2
20/02/19 > 17h02 > Cycle_B_78 >C-CV 140mA>2,25V>c-off 10mA ,pause 270mm ,C-CV 100mA>2,25V>c-off 10mA , D-CC 70mA>1,70v >625>> 1250mAh/dcm2
21/02/19 > 14h20 > Cycle_B_80 >C-CV 130mA>2,25V>c-off 10mA ,pause 270mm ,C-CV 100mA>2,25V>c-off 10mA , D-CC 70mA>1,70v >611>> 1222mAh/dcm2
22/02/19 > 11h00 > Cycle_B_81 >C-CV 130mA>2,25V>c-off 10mA ,pause 270mm ,C-CV 100mA>2,25V>c-off 10mA , D-CC 70mA>1,70v >607>> 1214mAh/dcm2
23/02/19 > 07h30 > Cycle_B_82 >C-CV 130mA>2,25V>c-off 10mA ,pause 270mm ,C-CV 100mA>2,25V>c-off 10mA , D-CC 70mA>1,70v >608>> 1216mAh/dcm2
25/02/19 > 04h06 > Cycle_B_83 >C-CV 130mA>2,25V>c-off 10mA ,pause 270mm ,C-CV 100mA>2,25V>c-off 10mA , D-CC 70mA>1,70v >655>> 1310mAh/dcm2
Sono arrivato alla capacità massima di 1378 mAh / dcm2.
Penso che sia il limite che possiamo sperare di ottenere da un tipo di lastra Planté
Immagine Allegata: objectif_max.jpg
Modificato da capi32 - 25/02/2019, 22:20:07
---------------
cugino della Francia
Inverter MPPsolar MPI 5.5Kw, 6480W pannelli, 4x100A PbCa e presto anche le batterie Planté ...
|
| | |
capi32
| Inviato il: 25/02/2019 22:17:11
|
la capacità di picco è leggermente superiore alla mia previsione (Fig. 129) ma la curva rimane simile.
questa diminuzione di capacità è dovuta al distacco (scaglie) del perossido dalla piastra positiva.
le scaglie sono + - 3mm sul lato.
con questo risultato, posso impostare il valore massimo della capacità di una batteria piantata a 1,3 Ah / dm2 di area positiva della piastra.
questo test di usura continua ma devo preparare rapidamente una nuova batteria per l'altro test ..
Immagine Allegata: Ecaillage.JPG
Modificato da capi32 - 06/07/2019, 00:51:30
---------------
cugino della Francia
Inverter MPPsolar MPI 5.5Kw, 6480W pannelli, 4x100A PbCa e presto anche le batterie Planté ...
|
| | |
ITA815
| Inviato il: 26/02/2019 00:30:30
|
Anche io sono sullo stesso livello per quello che riguarda l' accumulo ... difficile andare oltre. |
| | |
capi32
| Inviato il: 14/04/2019 10:29:06
|
dopo quasi 1 anno di cicli continui di carica e scarica, la batteria sembra essersi stabilizzata a + - 1,2Ah / dm2
che è un'ottima notizia e prefigura le basi della rinascita delle batterie di tipo Planté
.questo test di usura continua
Immagine Allegata: Cycle-b134.jpg
Modificato da capi32 - 06/07/2019, 00:51:06
---------------
cugino della Francia
Inverter MPPsolar MPI 5.5Kw, 6480W pannelli, 4x100A PbCa e presto anche le batterie Planté ...
|
| | |
ITA815
| Inviato il: 14/04/2019 11:58:05
|
Con che carico ?
C5 ? |
|
| | |
|